In the present study, the recyclability of the post-use milk pouches (50/50 LDPE-LLDPE blend) was evaluated with or without adding stabilizer. Thoroughly washed and dried post-use milk pouch films were extruded five times at high temperature (483-513 K) in the open atmosphere. The mode of degradation during extrusion operation was studied by melt flow index (MFI), theological properties, gel content and FT-IR analysis. The differential scanning calorimetry (DSC) analysis was carried out to evaluate the thermal stability of the stabilized and un-stabilized recycled mass from post-use milk pouch under this investigation. Mechanical properties (tensile strength, % elongation at break, tensile modulus and hardness) of the un-stabilized extruded material were significantly affected as a result of thermooxidative degradation during extrusion in presence of air. After all, stabilization with 0.4% anti-oxidant satisfactorily retains all the initial properties of the recycled material. (c) 2005 Elsevier B.V. All rights reserved.