Fracture toughness of adjacent flow weld lines, defined as weld lines that occur when two flow fronts meet and continue to flow together in the same direction (meld line or hot weld line), was evaluated by the single-edge notched-bend (SENB) method using three differently-shaped obstructive pins. Although the fracture toughness varied depending upon the shapes of the pin, the values could be standardized as the distance from the meeting point of the two flow fronts flowing around the pin. The fracture toughness decreased drastically from the meeting point along the weld line and then slightly increased. These characteristic features could be explained by flow-induced molecular orientation at the weld line interface. The molecules around the meeting point that were initially oriented parallel to the weld line due to fountain flow were able to relax, and then entanglement across the weld line interface developed because the flow stopped in the middle of the filling process, resulting in high fracture toughness. In contrast, the material at the downstream side of the weld line continued flowing during the filling process, being stretched along the flow direction. So, the molecular orientation at this area could not relax. In addition, the V-notch shape, i.e., the depth and length at the surface of the weld line, which also varied depending on the shape of the obstacles, was considered to be identical when the meeting point was allowed to be a datum point. Thus, the meeting point was found to be a significant factor when the properties of weld lines are investigated.