Silica xerogels were synthesized and annealed at 1000 degrees C for different durations to yield stable silica materials. The samples were prepared through base-catalyzed hydrolysis and condensation of tetramethyl orthosilicate in methanol. After aging and drying steps, clear and solid xerogels exhibiting a narrow pore size distribution were achieved. The annealincy treatment of these xerogels was performed at 1000 degrees C and proved in the present Study to lead to a monolithic glass when a progressive heat-treatment procedure was employed to attain 1000 degrees C. In addition to the expected glass, silica foams and ordered phases were observed when the samples were instantaneously heat-treated at 1000 degrees C. Raman spectra of the foamed materials exhibit the classical features of amorphous silica, whereas transmission electronic microscopy pictures reveal the presence of crystallized domains within the vitreous matrix. These crystallites are prone to nucleation and growth processes, which jeopardize the believed stability of the silica foam. The assessment of the hydroxyl content by IR spectroscopy reveals the role played by the latter polycondensation of silanols. The Occurrence of foaming process was thus found to result from two competitive phenomena occurring at 1000 degrees C: evacuation of water-related species and viscous sintering.