Highly crystalline single-phase nanoparticles of the important thermoelectric materials Zn4Sb3 and ZnSb were prepared from solvochemically activated powders of elemental zinc and elemental antimony. Low-temperature reactions with reaction temperatures of 275-300 degrees C were applied using an excess of elemental zinc. The nanoscale thermoelectrics obtained were characterized by X-ray powder diffraction, transmission electron microscopy, and thermal analysis. nc-Zn4Sb3 showed particle sizes of 50-70 nm, whereas particle sizes of 15-20 nm were observed for nc-ZnSb. Calorimetric investigations showed an increased heat capacity, C-p, for nc-Zn4Sb3 with respect to the bulk material which could be reduced to the bulk value by annealing nc-Zn4Sb3 at 190 degrees C. Interestingly, nc-Zn4Sb3 showed exothermic decomposition into zinc-poorer ZnSn at 196 degrees C in an open system, indicating that Zn4Sb3 is metastable in nanocrystalline form at room temperature.