Polyesters provide a good basis to work on for designing novel biodegradable materials that are also mechanically and thermally resistant. In this study, a series of aliphatic poly(ester amide)s (PEA) based on cyclohexane units was synthesized. Block-copolymers of cyclohexyl sebacate and cyclohexyl sebacamide were produced by controlling the length of the ester block and the amount of amide during a two-step melt/interfacial polycondensation reaction. Films produced from these materials could retain their shape above 373 K due to the physical network of amide hydrogen-bonding. Thermal properties were also evaluated, with various melting and softening points obtained depending on the PEA composition. The determining factor for mechanical properties was the amount of amide introduced, with films containing up to 10 mol % amide showing the best handleability and flexibility. Tensile properties typical of an amorphous viscoelastic material were observed, but with much superior elongation to break achievable (similar to 1700%). These materials were also shown to be hydrolyzable, noncytotoxic, and favorable for cell attachment: they may therefore have a promising future in the area of medical devices or packaging, especially as their properties can be tuned by changing their composition. (c) 2006 Wiley Periodicals, Inc.