A thermally labile polymer, poly(propylene glycol), was modified to obtain PPG having an amino end group. PPG was incorporated into a partially aliphatic polyimide based on an alicyclic dianhydride, and this afforded triblock copolymers containing various amounts of PPG blocks. The thermal properties of the copolymers were investigated by thermogravimetric analysis and differential scanning calorimetry. The thermal decomposition of the PPG block in the copolymers was carried out at 240 degrees C under various pressures to obtain porous polyimide films. The pores remained during the thermolysis under a reduced pressure of 710 mmHg, whereas they collapsed under (near) atmospheric pressure. The pore size increased as the amount of the PPG block in the copolymers increased. The dielectric constants of the porous polyimides varied from 2.60 to 2.42 with the original copolymer composition. (c) 2006 Wiley Periodicals, Inc.