We discuss the effect of screw rotation speed on the mechanical and rheological properties and clay dispersion state of polystyrene (PS)/organoclay (clay) nanocomposites prepared by melt compounding with a counter rotating-type twin-screw extruder. Poly(styrene-co-vinylox-azolin) (OPS) was used as an additional material. The Young's modulus of the PS/OPS/clay nanocomposites showed the maximum value at a screw rotation speed of 70 rpm in this study. This implied the existence of an optimized screw rotation speed for the melt compounding of the polymer/clay nanocomposites. For PS/clay systems without the addition of OPS, the peak intensity from clay increased and the distance between clay platelets in the nanocomposites decreased with the screw rotation speed. On the other hand, inverse results were obtained for PS/OPS/clay systems. According to the transmission electron microscopy photographs, the PS/OPS/clay nanocomposite at 70 and 100 rpm had fully exfoliated clay platelets. The dynamic rheological properties of the PS/clay nanocomposites were almost the same as those of neat PS. On the other hand, the storage and loss moduli of the PS/OPS/clay nanocomposites at the same frequency were larger than those of the PS/clay system. On the whole, the bonding between clay platelets and PS was important for increasing the viscosity and elasticity in the melts of the PS/clay system. (c) 2006 Wiley Periodicals, Inc.