In the past several types of synthetic porous materials have been made as meniscus reconstruction materials. Most of these materials lacked a good combination between suitable mechanical properties and a high interconnectivity. In this work porous scaffolds were made from the polyurethane Estane 5701-F1 by freeze drying of a dioxane and water solution in combination with salt leaching. It was possible to obtain very porous scaffolds with a very high interconnectivity. Porosity, pore size and interconnectivity can be independently adjusted by varying the amount of water, porogen size and the amount of porogen used. The obtained compression moduli of the scaffolds were between 40 kPa and 400 kPa with a variation in porosity between 72 and 87%. These scaffolds are very suitable for the use as meniscus replacement materials. (c) 2006 Springer Science + Business Media, Inc.