The superparamagnetic properties of CoFe2O4 and Fe3O4 nanocrystals have been systematically investigated. The observed blocking temperature of CoFe2O4 nanocrystals is at least 100 deg higher than that of the same sized Fe3O4 nanocrystals. The coercivity of CoFe2O4 nanocrystals at 5 K is over 50 times higher than the same sized Fe3O4 nanocrystals. The drastic difference in superparamagnetic properties between the similar sized spherical CoFe2O4 and Fe3O4 (or FeFe2O4) spinel ferrite nanocrystals was correlated to the coupling strength between electron spin and orbital angular momentum (L-S) in magnetic cations. Compared to the Fe2+ ion, the effect of much stronger spin-orbital coupling at Co2+ lattice sites leads to a higher magnetic anisotropy and results in the dramatic discrepancy of superparamagnetic properties between CoFe2O4 and Fe3O4 nanocrystals. These results provide some insight to the fundamental understanding of the quantum origin of superparamagnetic properties. Furthermore, they suggest that it is possible to control the superparamagnetic properties through magnetic coupling at the atomic level in spinel ferrite nanocrystals for various applications.