Titania and titania-silver nanoparticle deposits were made by Liquid Flame Spray technique, in which the liquid precursor is injected into a high temperature flame, where it will evaporate and nucleate to nanosize particles. One-step and two-step methods were used for preparation of titania-silver deposits. The amount of silver added was 1 wt%. The deposits were collected in the flame zone on steel and glass surfaces and were analyzed by TEM, EDS, XPS and SAXS. The titania deposits consisted of porous nanosized titania agglomerates of primary particles (similar to 10 nm). With silver addition, small spherical silver metal particles (similar to 2 nm) were detected on the agglomerates. An increase in the photocatalytic activity was verified by stearic acid decomposition and biofilm removal using Deinococcus geothermalis as the model organism.