YSZ thin films were grown evaporating cubic and tetragonal phase ZrO2 stabilized by 8 Wt-% of Y2O3 (8% of YSZ) ceramic powders by using e-beam deposition technique. Operating technical parameters that influence thin film properties were studied. The influence of substrate crystalline structure on growth of deposited YSZ thin film was analyzed there. The YSZ thin films (1.5-2 mu m of thickness) were deposited on three different types of substrates: Al2O3, optical quartz (SiO2), and Alloy 600 (Fe-Ni-Cr). The dependence of substrate temperature, electron gun power, and phase of ceramic powder on thin film structure and surface morphology was investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The substrate temperature was changed in the range of 20-600 degrees C (during the YSZ thin film deposition) and its influence on the crystallinity of deposited YSZ thin films was analyzed. It was found that electron gun power and substrate temperature has the influence on the crystallite size, and texture of YSZ thin films. Also, the substrate has no influence on the crystal orientation. The crystallite size varied between 20 and 40 nm and increased linearly changing the substrate temperature. The crystal phase of evaporated YSZ powder has the influence on the structure of the deposited YSZ thin films. (c) 2005 Elsevier B.V. All rights reserved.