The properties of catalysts with (i) Bronsted-type acidity (H-mordenite and Al/P mixed oxide), (ii) Lewis-type acidity (At trifluoride) or (iii) basic characteristics (Mg/Fe mixed oxide) were investigated in the gas-phase methylation of catechol. When methanol was used as the methylating agent, H-mordenite and AlF3 gave high selectivities to guaiacol (the product of O-methylation) under mild reaction conditions, that is at very low catechol conversions. An increase in temperature led to the transformation of guaiacol to phenol and cresols, and to considerable catalyst deactivation. The basic catalyst Mg/Fe/O also favored an extensive degradation of guaiacol to phenol. On the mildly acidic catalyst Al/P mixed oxide a stable catalytic perfon-nance and a high selectivity to guaiacol at 40% catechol conversion were obtained. When methylformate, a more reactive methylating agent, was used with AlF3 and Mg/Fe mixed oxide as catalysts, higher catechol conversions and slower deactivation rates could be achieved under mild reaction conditions, with a low extent of guaiacol degradation. However, methylformate rapidly decomposed when temperatures above 350 degrees C were used. Finally, tests were made by reacting catechol and diethoxymethane with acid catalysts, with the aim of synthesizing methylenedioxybenzene. The latter product was obtained with high selectivity, but with very low yield, due to both catalyst deactivation and decomposition of diethoxymethane. (c) 2006 Elsevier B.V. All rights reserved.