Dilute acid hydrolysis studies were performed on forest residues of Eucalyptus grandis, in a cylindrical reactor of stainless steel. The kinetics of this hydrolysis reaction was investigated employing 0.65% sulfuric acid, a residue/acid solution ratio of 1/9 (w/w), temperatures of 130, 140, 150, and 160 degrees C, and reaction times in the range 20-100 min. The results showed that, under the optimized conditions of acid hydrolysis employed in this study, the variables temperature and reaction time had a strong influence on hemicellulose removal and a small influence on the degree of lignin and cellulose removal. The highest xylose extraction yield was 87.6% attained at 160 degrees C, after 70 min reaction time, simultaneously with the formation of decomposition products, namely 2.8% acetic acid, 0.6% furfural, and 0.06% 5-hydroxymethylfurfural. A similar xylose extraction yield (82.8%) was observed at 150 degrees C after 100 min, with the formation of 3.2% acetic acid, 1.0% furfural, and 0.07% 5-hydroxymethylfurfural. The kinetic parameters determined at 130, 140, 150, and 160 degrees C for degradation of xylan present in the hemicellulose of the eucalyptus forest residue during the formation of xylose were the first-order reaction rate constants (k) for each temperature, 1.22 x 10(-4), 2.12 x 10(-4), 5.43 x 10(-4), and 9.05 x 10(-4) s(-1), respectively, and an activation energy (E-a) of 101.3 kJ mol(-1).