We report here direct contact membrane distillation results from modules having 0.28 m(2) of membrane surface area employing porous hydrophobic polypropylene hollow fibers of internal diameter (330 mu m) and wall thickness (150 mu m) with a porous fluorosilicone coating on the outside surface. The brine salt concentration and temperature and the distillate temperature and velocity were varied. Water vapor fluxes approach values obtained earlier in much smaller modules. As the brine temperature was increased from 40 to 92 degrees C, water vapor flux increased almost exponentially. Increasing the distillate temperature to 60 from 32 degrees C yielded reasonable fluxes. Salt concentration increases to 10% led to a small flux reduction. An extended 5-day run did not show any pore wetting. A model using the mass transfer coefficient k(m) as an adjustable parameter predicted the brine temperature drop, distillate temperature rise, and water vapor flux well for the large module and the smaller module of 119-cm(2) surface area.