In this paper, the investigation of surface forces in semidilute solutions of a nonadsorbing hydrogen-bonded reversible supramolecular polymer is described. Colloidal probe atomic force microscopy was used for direct measurement of depletion forces. Hydrodynamic drag on the AFM cantilever with the colloidal probe was measured both far away from and close to the planar substrate surface. The results indicate that the presence of the depletion layer causes slip at the surfaces with a large apparent slip length. Our analysis explains how the presence of slip enables the measurement of (relatively weak) depletion forces in solutions with a high viscosity by significantly reducing the hydrodynamic forces. The range and magnitude of the measured depletion forces are qualitatively in agreement with previous experiments and theoretical predictions. Due to the relatively large experimental error, no quantitative conclusions can be drawn. Depletion-induced phase separation of suspensions of stearylated silica particles was also observed. Phase separation becomes more pronounced with increasing polymer concentration.