SBT films with different thickness were fabricated using a sol-gel processing and spin coating. The as-coated films were heated at 600 degrees C for the crystallization to fluorite and then further heated at 740-770 degrees C for the phase transformation to Aurivillius. It was found that the phase transformation kinetics apparently increased with thickness up to similar to 390 nm, and then it decreased above this value. The Johnson-Mehi-Avrami (JMA) isothermal kinetics analyses showed the dependence of nucleation and crystal growth modes on the film thickness. From the Arrhenius plots the activation energy values for the phase transformation were determined for SBT films with different thickness. (c) 2005 Elsevier B.V. All rights reserved.