The aim of this study is to investigate the effect of four metal nitrate contaminants, namely chromium, manganese, lead and zinc on the mechanical and leaching characteristics of cement-based materials. For this purpose, three different matrices made of: (i) Portland cement, (ii) Portland cement and silica fume, and (iii) Portland cement and natural zeolite were studied. The effects of metals on the stabilised/solidified (S/S) product characteristics were monitored by measuring: (i) setting time, (ii) compressive strength, (iii) acid neutralisation capacity (ANC), and (iv) solubility of the metal contaminants as a function of pH. The results of both mechanical and leaching tests showed the importance of the contaminant/matrix couple considered. Setting time was accelerated in presence of chromium, while in presence of manganese, lead and zinc it was delayed. However, for the last two contaminants, a 10% replacement of cement by silica fume and zeolite, markedly accelerated the setting time compared to the cement-only matrix. Although the early strength development was adversely affected in presence of all four contaminants, the long-term strength was less affected compared to the control materials. Although the ANC of the materials was not markedly affected by the presence of contaminants, the nature of the matrix did modify the ANC behaviour of the solidified materials. The increased strength and reduced ANC observed in the presence of silica fume are both due to pozzolanic reaction. The type of matrix used for solidification did not affect the solubility of the four metal contaminants. Overall, the results showed that the use of blended cements must be carried out with care and the performance assessment of waste-containing cement-based materials must take into consideration both the mechanical and leaching characteristics of the systems. (C) 2002 Elsevier Science B.V. All rights reserved.