The percolation leaching of the Cuban nickel tailings containing 0.34% Ni, 0.08% Co and 44.2% Fe was investigated by using tartaric and oxalic acids at different concentrations. About 70% Ni, 80% Co and 30% Fe were extracted after 5 days of leaching with the mixture of 0.15 mol/L tartaric acid and 0.05 mol/L oxalic acid at ambient temperature and normal pressure. Nickel and cobalt extraction of 80% as well as iron extraction of 50% were achieved from the pregnant solution by means of precipitation at 80 degrees C for 2 It. The precipitation at ambient temperature led to a similar result after 16 days. Cobalt, nickel and iron oxalates were found in the precipitate by using the X-ray diffraction method. The regeneration of acids during the precipitation step made possible the reuse of the raffinate at the leaching step. Heating of the precipitate at 200 degrees C increased the metal concentration to 1.22% Ni and 0.33% Co, which can be fed in the existing nickel plant in Moa, Cuba. The magnetic processing of the leaching residues led to a non-magnetic product containing less than 20% Fe and a magnetic product containing more than 50% Fe. (c) 2006 Elsevier B.V. All rights reserved.