The present work presents preliminary results concerning ordinary portland cement (OPC) blended with electric-arc-furnace dust (EAFD) obtained from steel-smelting plants. The powder obtained after acid treatment of the EAFD consisted basically of nanometer-sized particles of ZnFe2O4. Incorporation of the EAFD in the OPC produced retardation of the setting process. Nevertheless, after 7 d, the compressive strength of the OPC/EAFD pastes was superior to undoped OPC, and, after 28 d, the extent of hydration of the OPC/EAFD pastes was equivalent to undoped OPC. A compressive strength of 72 MPa was attained after 42 d for OPC doped with 10 wt% EAFD.