Three-dimensional textile Hi-Nicalon SIC-fiber-reinforced SiC composites were fabricated using chemical vapor infiltration. The microstructure and mechanical properties of the composite materials were investigated under bending, shear, and impact loading. The density of the composites was 2.5 g.cm(-3) after the three-dimensional SiC perform was infiltrated for 30 h. The values of flexural strength were 860 MPa at room temperature and 1010 MPa at 1300degreesC under vacuum. Above the infiltration temperature, the failure behavior of the composites became brittle because of the strong interfacial bonding and the mismatch of thermal expansion coefficients between fiber and matrix. The fracture toughness was 30.2 MPa.m(1/2). The obtained value of shear strength was 67.5 MPa. The composites exhibited excellent impact resistance, and the dynamic fracture toughness of 36.0 kJ.m(-2) was measured using Charpy impact tests.