Ceramic foams with porosity exceeding 90% were prepared by direct foaming and casting of aqueous suspensions containing cetyl trimethyl ammonium bromide (CTAB) as a foaming agent. Foaming of the suspensions, particularly with lower viscosity, was initially non-homogeneous but the foam appeared to homogenize with milling time. Addition of sucrose to ceramic suspensions resulted in lowering of the suspension viscosity, stabilized the foams by reducing drainage of the suspension, and minimized coalescence of bubbles leading to lower cell sizes in sintered foams. Ceramic foams prepared from sucrose based suspensions were strengthened to such an extent that foams with porosity above 90% could be machined in the green state.