AlN-SiC solid solution particles with a variety of morphologies including faceted polyhedrons with or without ledges; hexagonal platelets; hexagonal columns with a hexagonal plate or a pyramidal cap; and interpenetrating cones, have been found in the combustion products of a mixture of Al, Si, and carbon black under a nitrogen pressure of 10 MPa. Combustion temperature (the growth temperature of crystals) is the most important factor controlling the morphology of crystals formed in the combustion product. When temperatures are close to the melting point of the solid solutions, a small driving force for nucleation and long distances of surface migration make nucleation on the basal plane difficult, and thus the solid solution particles tend to grow as platelets. Supersaturation is the second key factor influencing crystal growth. At relatively low temperatures, a low supersaturation at the large pores renders nucleation difficult and the solid solution particles tend to grow as platelets. At relatively low temperatures and high supersaturation, a relatively high driving force for nucleation and short mean distances of surface migration promote the growth of AlN-SiC solid solutions as polyhedrons. The formation of the ledges on the polyhedral particles is attributed to the differences in the evaporation rates and the deposition rates between Al and Si. At relatively low temperatures and an intermediate supersaturation, the solid solution particles grow as prismatic columns. The formation of the prismatic columns with a hexagonal plate, or a pyramidal cap, is attributed to a sudden change of temperature during combustion. A possible growth mechanism for the AlN-SiC solid solution cones is proposed.