Sb-doped SnO2 films have been prepared by the sol-get method with the colloidal precursors. The colloidal precursors were prepared by adding urea into the SnCl4 and SbCl3 aqueous solution. The crystalline structure of the colloidal particles and the films are rutile-type structure examined by X-ray diffraction technique. The dependencies of electrical properties of the films on the firing temperature and Sb content have been studied. Conductivity and carrier concentration increase as the Sb concentration increases from 0 to 10%. The transmittance of the films firing at 600 degreesC was about 92% in the 450-800 nm wavelength range. (C) 2004 Elsevier B.V. All rights reserved.