A lead-free ferroelectric material, (K(0.5)B(3)i(0.5))TiO3 (KBT), was prepared by a sol-gel process. Thermal analysis and X-ray diffraction showed that perovskite KBT powders with a grain size of 100-200 nm were obtained by calcining dried gels above 700 degrees C. When the calcining temperature was lower than 650 degrees C, only the Bi2Ti2O7 phase was found in the X-ray diffraction patterns. Moreover, KBT ferroelectric ceramics was fabricated by traditional sintering of as-prepared KBT powders. The KBT ceramics sintered at 1050 degrees C showed a high density (91.2% of theoretic density) and low dielectric loss, better than that prepared by a solid-state reaction method. The temperature dependence of dielectric permittivity of KBT ceramics showed a Curie temperature at 385 degrees C. (c) 2005 Elsevier B.V. All rights reserved.