A low-temperature Si0.8Ge0.2 (LT-Si0.8Ge0.2) interlayer was grown at 500 degrees C to improve the relaxed Si0.8Ge0.2 surface and reduce the dislocation density in it, which was confirmed by the change of reflective high-energy electron diffraction (RHEED) pattern from spotty to streaky and etch pits counts. For the same extent of strain; the threading dislocation density was reduced from 8 x 10(7) cm(-2) in the latter to 2 x 10(6) cm(-2) in the former.