Solvothermal preparation of graphite-like C3N4 nanocrystals

Bai YJ; Lu B; Liu ZG; Li L; Cui DL; Xu XG; Wang QL

Journal of Crystal Growth, Vol.247, No.3-4, 505-508, 2003

DOI10.1016/S0022-0248(02)01981-4 Export Citation

Solvothermal preparation of graphite-like C3N4 nanocrystals

Bai YJ, Lu B, Liu ZG, Li L, Cui DL, Xu XG, Wang QL

Graphite-like C3N4 nanocrystals were synthesized by the reaction Of CCl4 and NH4Cl at 400degreesC without any catalyst. XRD and TEM examinations indicate that the average size of the crystals is about 11 nm With a good crystallinity, and C = N and C-N bonds can be observed at 1617.95 and 1271.09 cm(-1) respectively, in the IR spectrum. (C) 2002 Elsevier Science B.V. All rights reserved.

Keywords:transmission electron microscope;X-ray diffraction;nanomaterials;infrared devices