The fabrication of high quality superconducting thin films using pulsed laser deposition (PLD) has been reported to find optimized processing conditions and to make millimeter-wave devices. High temperature superconducting (HTS) YBCO films were prepared on MgO (10 mm x 10 mm x 0.5 mm) substrates by PLD, The 3-pole bandpass filter centered at 22 GHz for satellite communication was designed consisting of hairpin type coupled-lines to reduce the configuration in size. YBCO films are c-axis oriented and show superconductive transition temperatures of 88-89 K with the transition widths <0.5 K. The insertion loss of passband at 70 K was about 5 dB. The measured frequency response of superconducting filter will be compared with the simulation result,