The influence of the SiCp proportion and the matrix concentration of four aluminium metal matrix composites (A360/SiC/10p, A360/SiC/20p, A380/SiC/10p, A380/SiC/20p) modified by lanthanum-based conversion or electrolysis coating was evaluated in neutral salt fog according to ASTM B 117. Lanthanum-based conversion coatings were obtained by immersion in 50 degrees C solution of La(III) salt and lanthanum electrolysis treatments were performed in ethylene glycol mono-butyl ether solution. These treatments preferentially covered cathodic areas such as intermetallic compounds, Si eutectic and SiCp. The kinetic of the corrosion process was studied on the basis of gravimetric tests. Both coating microstructure and nature of corrosion products were analyzed by scanning electron microscopy (SEM), atomic force microscopy (AFM), energy dispersive X-ray analysis (EDS) and low angle X-ray diffraction (XRD) before and after accelerated testing to determine the influence of microstructural changes on corrosion behaviour during exposure to the corrosive environment. The corrosion process was more influenced by the concentration of alloy elements in the matrix than by the proportion of SiCp reinforcement. Both conversion and electrolysis surface treatments improved the behaviour to salt fog corrosion in comparison with original composites without treatment. Additionally, electrolysis provided a higher degree of protection than the conversion treatment because the coating was more extensive. (c) 2005 Elsevier B.V. All rights reserved.