The surface of gloss fired porcelain with and without raw glaze coating was radiated by a CO2 laser working at 10.6 mu m, a choice resulted from spectroscopic studies of suspensions made of China. The shine of the untreated sample was defined as the distribution of micro-droplets on the surface. The surface alterations due to laser heating were classified by the diameter of the completely melted surface, the ring of the surface at the threshold of melting, and the size of microscopic cracks. The diameter of the laser treated area was in the range of 3 mm, while the incident laser power and the duration of laser heating were varied between 1 and 10 W and 1-8 min, respectively. The different stages of surface modifications were attributed primarily to the irradiating laser power and proved to be rather insensitive to the duration of the treatment. We have found a range of parameters under which the white China surface coated with raw glaze and followed by laser induced melting exhibited very similar characteristics to the untreated porcelain. This technique seems prosperous for laser assisted reparation of small surface defects of unique China samples after the firing process. (c) 2005 Elsevier B.V All rights reserved.