The paper is devoted to investigating the formation of CuCl and regenerated Cu crystals on bronze. Electrochemical behaviour of bronze in simulated anoxic edaphic media and occluded cell (O.C.) solutions was studied with cycle voltammetry (CV) and X-ray diffraction (XRD). Within potential range of -800 to +800 mV, oxidation occurred was largely a process in which Cu is oxidized to CuCl and the reduction process was a reverse of it. An atomic force microscopy (AFM) was used to observe the morphology of CuCl crystals, regenerated Cu crystals and corrosion interface at nm level. The deposition of regenerated Cu on simulated archaeological bronzes was simulated under experimental conditions for the first time. CuCl could be thoroughly reduced to pure Cu if reduction time interval were sufficiently prolonged. This provided a theoretical and experimental basis for getting rid of harmful CuCl patina from archaeological bronzes with electrochemical means. (c) 2005 Elsevier B.V. All rights reserved.