The corrosion inhibition of 1-(2-pyridylazo)-2-naphthol (PAR) on the corrosion of cold rolled steel in 0.5 M sulfuric acid (H2SO4) was studied using weight loss method and potentiodynamic polarization method. Results obtained revealed that together with chloride ion, PAR is an effective corrosion inhibitor for steel corrosion in sulfuric acid. It was found that for steel corrosion inhibition in the presence of single PAR in sulfuric acid the Temkin adsorption isotherm may be used to explain the adsorption phenomenon. For the mixture of PAR and NaCl used as corrosion inhibitor, however, the Langmuir adsorption isotherm can be used to satisfactorily elucidate the adsorption of mixture of PAR and NaCl. Potentiodynamic polarization studies showed that single PAR mainly acts as a cathodic inhibitor for the corrosion of steel in 0.5 M sulfuric acid. The mixture of PAR and chloride ion, however, acts as a mixed type inhibitor that mainly inhibits cathodic reaction of the steel corrosion in sulfuric acid. By means of electrochemical polarization tests, a desorption potential at ca. -370 mV was observed for the adsorption of mixture of PAR and chloride ion, when potential reaches this value, adsorbed inhibitor molecule heavily departs from the steel surface. For the mixture of PAR and chloride ion, thermodynamic parameters such as adsorption heat, adsorption entropy and adsorption free energy were obtained from experimental data of the temperature studies of the inhibition process at four temperatures ranging from 30 to 45 degrees C, the kinetic data such as apparent activation energies and pre-exponential factors at different concentrations of the inhibitor were calculated, and the effect of the apparent activation energies and pre-exponential factors on the corrosion rates of cold rolled steel was discussed. The most suitable range of inhibitor concentration was discussed. The inhibitive action was satisfactorily explained by using both thermodynamic and kinetic models, Synergism between chloride ion and PAR was proposed. The results obtained from weight loss and potentiodynamic polarization were in good agreement. (c) 2006 Elsevier B.V. All rights reserved.