Studying the surface properties of cubic boron nitride (c-BN) thin films is very important to making it clear that its formation mechanism and application. In this paper, c-BN thin films were deposited on Si substrates by radio frequency sputter. The influence of working gas pressure on the formation of c-BN thin film was studied. The surface of c-BN films was analyzed by X-ray photoelectron spectroscopy (XPS), and the results showed that the surface of c-BN thin films contained C and O elements besides B and N. Value of N/B of c-BN thin films that contained cubic phase of boron nitride was very close to 1. The calculation based on XPS showed that the thickness of hexagonal boron nitride (h-BN) on the surface of c-BN films is approximately 0.8 nm. (c) 2005 Elsevier B.V. All rights reserved.