InGaAs layers on undoped GaAs (0 0 1) substrates were grown by atmospheric pressure metalorganic vapour phase epitaxy (AP-MOVPE). In order to obtain films with different indium composition (x(ln)), the growth temperature as a growth parameter, was varied from 420 to 680 degrees C. Furthermore, high-resolution X-ray diffraction (HRXRD) measurements were used to quantify the change of x(ln). Crystal quality has been also studied as a function of growth conditions. On the other hand, laser reflectometry (LR) at 632.8 nm wavelength, was employed to in situ monitor epitaxy. Reflectivity-time signal was enabled to evaluate structural and optical properties of samples. We have fitted experimental data to determine optical constants and growth rate of InGaAs at 632.8 nm. In addition, the fitting provided InGaAs thickness as a function of growth time. Based on ex situ characterization by scanning electronic microscopy (SEM) and HRXRD, we propose a practical method, relating the contrast of first reflectivity maximum with the X-ray diffraction peak angular difference between the substrate and epitaxial layer, to determine in situ the In solid composition in InGaAs alloys. (c) 2006 Elsevier B.V. All rights reserved.