Microhardness (H) of gelatin dry cast films was measured in the 100-250 degrees C range. A strong H increase with temperature from 330 MPa up to 450 MPa was observed in the first cycle. The H values reached in the subsequent cycles are higher than those obtained in the preceding ones, surpassing the hardness of all commercial synthetic polymers and soft metals. Results are discussed in terms of crosslinking between side-chain reactive groups.