Direct dehydration polycondensation of dicarboxylic acids and alcohols was carried out by surfactant-combined Bronsted and Lewis acids. This procedure did not require the removal of water, because the esterification was established at the interface of the emulsion in water. Emulsion polycondensations of 1,9-nonanediol (1,9-ND) and dodecanedioic acid (DDA) (the molar ratio of dicarboxylic acid to diol 1:1) were carried out at 80 degrees C for 48 h in the presence of 16 wt % DBSA. The corresponding polyester (M-w 10.1 X 10(3)) was obtained in an excellent yield (99%). Chain extension in the emulsion was carried out using hexamethylene diisocyanate as the chain extender. SEC measurements indicated the expected shift to higher molecular weight region (M-w = 11.4 x 10(3), M-w/M-n = 3.4) compared with parent polyester (M-w = 4.5 x 10(3), M-w/M-n = 2.2).