Application of shear and cross-linking enzyme transglutaminase (Tgase) induced fibrous hierarchical structures in dense (30% w/w) calcium caseinate (Ca-caseinate) dispersions. Using Tgase was essential for the anisotropic structure formation. The fibrous materials showed anisotropy on both micro- and macroscale as determined with scanning electron microscopy (SEM) and mechanical analyses, respectively. SEM revealed protein fibers with a diameter of similar to 100-200 nm; visually, we observed fibers of about 1 mm. Both shear and Tgase affected the reinforcement of the fibers to a large extent, whereas the mechanical properties in the direction perpendicular to the shear flow remained constant. Shearing Ca-caseinate without Tgase yielded a slightly anisotropic layered structure. Both cross-linking in the absence of shear and cross-linking during mixing resulted in gels without alignment. The formation of shear- and enzyme-induced anisotropic structures was explained by aligning of protein aggregates due to shear and concurrent solidification of the aligned protein aggregates.