How fibroin molecules fold themselves and further self-assemble into aggregations with specific structures when the solution concentration increases is the key to understanding the natural silk-forming process of the silkworm. A regenerated Bombyx mori silk fibroin solution was prepared, and serially diluted solutions were coated on aminated coverslips. Atomic force microscopy (AFM) observations of the topography of fibroin molecules revealed a transformation from rodlike aggregations 100-200 nm long to small globules 50 mn in diameter with decreasing concentrations. When the incubation duration increased, the aggregations of fibroin molecules showed a self-assembling process, which was measured with AFM. In particular, after the molecules were incubated for more than 20 min, rodlike micelles formed and were distributed evenly on the surface of the aminated slides. Flow chamber technology was used to study the effect of the shear loading on the topography of the fibroin molecular aggregations. After a shear loading was applied, larger rodlike particles formed at a higher incubation concentration in comparison with those at a lower concentration and were obviously oriented along the direction of fluid flow.