3,3-Dichloro-N,N'-biphthalimide (3,3'-DCBPI), 3,4'-dichloro-N,N'-biphthalimide (3,4'-DCBPI), and 4,4'-dichloro-N,N'X-biphthalimide (4,4'-DCBPI) were synthesized from 3-or 4-chlorophthalic anhydrides and hydrazine in glacial acetic acid. The yield of 3,3'-DCBPI (90%) was much higher than that of 4,4'-DCBPI (33%) because of the better stability of the intermediate, 3-chloro-N-aminophthalimide, and 3,3'-DCBPI. A series of hydrazine-based polyimides were prepared from isomeric DCBPIs and 4,4-thiobisbenzenethiol (TBBT) in N,N-dimethylacetamide in the presence of tributylamine. Inherent viscosity of these polymers was in the range of 0.51-0.69 dL/g in 1-methyl-2-pyrrolidinone (NMP) at 30 degrees C. These polyimides were soluble in 1,1,2,2-terachloroethane, NMP, and phenols. The 5% weight-loss temperatures (T(g)s) of the polymers were near 450 degrees C in N-2. Their glass-transition temperatures (T(g)s) determined by dynamic mechanical thermal analysis and differential scanning calorimetry increased according to the order of polyimides based on 4,4'-DCBPI, 3,4'-DCBPI, and 3,3'-DCBPI. The hydrolytic stability of these polymers was measured under acid, basic, and neutral conditions and the results indicated that the order was 3,3'-DCBPI/TBBT > 3,4'-DCBPI/TBBT > 4,4'-DCBPI/TBBT. (c) 2007 Wiley Periodicals, Inc.