Fe-Ni-W alloys with 18 wt%, 35 wt% and 55 wt% tungsten have been obtained by electrodeposition from an ammoniacal citrate bath. The deposits are smooth, of nice appearance, and adhere well to iron and steel. The morphology and structure of Fe-Ni-W alloys were studied by SEM and XRD, respectively. The structure of the as-plated deposits changed from crystalline to amorphous with increasing tungsten content. The amorphous structure crystallized under heat treatment condition. The wear and corrosion resistance of the deposits were tested by MPX-2000 weartear equipment and neutral salt spray test (NSS), respectively. The alloys with 55 wt% tungsten, after heat treatment at proper temperatures, appear to have good wear resistance and hardness. The alloys with 18 wt% tungsten are very corrosion-resistant. (c) 2007 Elsevier B.V. All rights reserved.