A set of AMIN multilayers with various modulation periods were prepared using DC magnetron sputtering method. Low angle X-ray diffraction (LAXRD) was used to analyze the layered structure of multilayers. The phase structure of the films was investigated with grazing angle X-ray diffraction (GAXRD). LAXRD results indicate that well-defined multilayer modulation structures are formed for the relatively larger modulation periods. However, the loss of mutilayered structure is detected in the multilayer with low modulation period. A very wide amorphous peak is observed in multilayer with modulation period of 4 nm. The multilayers show obvious crystallization at larger modulation periods, however, the diffraction peaks are much wider than the Al single layer because of the interruption of the continuous columnar grain growth by alternating deposition processes. Nanoindentation experiments were performed to study the mechanical properties as a function of multilayer modulation period. It is found that the hardness of the multilayers is greater than the hardness calculated from rule of mixtures. With the modulation periods adjusted, the multilayers are even harder than its hard component (AlN). A maximum hardness of 24.9 GPa, about 1.9 times larger than its hard component (AlN) and 3.7 times larger than the hardness calculated from the rule of mixtures, is found at the multilayer with modulation period of 16 nm. The wear test results show that the multilayers possess lower and stable friction coefficient, and superior wear properties. (c) 2007 Published by Elsevier B.V.