In this study, the electrical discharge machining (EDM) of titanium alloy (Ti-6Al-4V) with different electrode materials namely, graphite, electrolytic copper and aluminium and process parameters such as, pulse current and pulse duration were performed to explore the influence of EDM parameters on various aspects of the surface integrity of Ti6Al4V Scanning electron microscopy (SEM), X-ray diffraction (XRD), energy dispersive spectrograph (EDS) and hardness analysis were performed. The experimental results reveal that the value of material removal rate, surface roughness, electrode wear and average white layer thickness are tendency of increase with increasing current density and pulse duration. However, extremely long-pulse durations such as 200 lis led to decrease MRR and surface roughness. Furthermore, the surface hardness is increasing due to the Ti24C15 carbides formed on the surface and obvious cracks are always evident in re-solidified layer when machining copper electrode. The surface crack densities and critical crack lines were determined for the tested material. The graphite electrode is beneficial on material removal rate, electrode wear and surface crack density but relatively poorer surface finish. (c) 2007 Elsevier B.V. All rights reserved.