The work addresses the influence of cementation and electrodeposition of copper coatings on the corrosion resistance of AISI 304 stainless steel immersed in 30 wt.% H2SO4 at temperatures of 25 and 50 degrees C. Corrosion process was evaluated by gravimetric tests, DC measurements and electrochemical impedance spectroscopy (EIS). The specimen surfaces were analysed by scanning electron microscopy, X-ray photoelectron spectroscopy (XPS) and X-ray diffraction. The corrosion performance of AISI 304 stainless steel in sulphuric acid solution was g-,really improved by copper coatings. The amount of copper deposited by the cementation process was sufficient to protect the stainless steel of corrosion. A greater amount of copper obtained by electrodeposition treatments does not supply further improvement in the corrosion behaviour. The improved corrosion resistance is related to copper dissolution at the initial stages of immersion tests and the presence of Cu2+ in the solution, which makes the medium more oxidizing, increasing the stability of the passive layer. In addition, the presence of copper at the surface reduces the overpotential of cathodic reaction, enabling the transition from an active region to the passive one. (c) 2007 Elsevier B.V. All rights reserved.