High-temperature (HT) AIN films were grown on (0 0 0 1) sapphire by low-pressure flow-modulated (FM) metal organic vapor phase epitaxy (MOVPE) with and without inserting a thin medium-temperature (MT) AIN layer. To suppress parasitic reactions between the sources of trimethylaluminum (TMA) and ammonia (NH3), TMA and NH3 was introduced to the reactor of MOVPE by alternating supply way. Surface morphology and crystalline quality were characterized by a scanning electronic microscopy (SEM), atomic force microscopy (AFM) and X-ray rocking curve (XRC) measurements of (0 0 0 2) and (10-12) diffractions. The AFM and SEM measurements indicated that the thin MT-AIN layer had a strong influence on the surface morphology of the HT-AIN films. The surface morphology became quite smooth by inserting the thin MT-AIN layer and surface RMS roughness values were 0.84 nm and 13.4 nm for the HT-AIN films with and without inserting the thin MT-AIN buffer layer, respectively. By etching the samples in aqueous KOH solution, it was found that the polarity of AIN films was different, the HT-AIN film with the thin MT-AIN layer could not be etched, indicating that the film had an M-polar surface; however, the film without the MT-AIN layer was etched, which was explained that that film had a N- or mixed-polar surface. The mechanism for the origin of the different polarity of HT-AIN with and without the thin MT-AIN layer was proposed and discussed in detail. (C) 2007 Elsevier B.V. All rights reserved.