The dentin quality of primary and permanent teeth was inspected by Fourier transformed Raman spectroscopy (FT-Raman); scanning electron microscopy/energy-dispersive spectroscopy (SEM/EDS) and hardness test. Middle dentin of crowns were reached by carbide bur abrading providing a uniform smear layer. Phosphoric acid was applied in order to simulate the etching of total etching adhesive systems. The groups were (n = 10): G1 (primary dentin smear layer); G2 (35% phosphoric acid etched primary dentin); G3 (permanent dentin smear layer); G4 (35% phosphoric acid etched permanent dentin). FT-Raman results were subjected to cluster analysis. SEM/EDS were made in order to add the data obtained by FT-Raman. The hardness data were subjected to ANOVA and Tukey test. FT-Raman showed differences among groups, either to organic or inorganic content. For the organic content, primary and permanent dentin became similar after the etching; conversely, the inorganic content showed differences for the two substrates. Hardness test showed no significant differences between primary and permanent dentin, before or after etching, but the etching decreased these values. The mineral content arrangement of primary dentin is different from permanent dentin, independently of the etching. The substrate type did no influence the hardness, but the etching decreased it. (c) 2007 Elsevier B.V. All rights reserved.