Two syndiotactic polypropylene (sPP) sample films (S-0 and S-90) with different initial structures were prepared in this paper by isothermal crystallization from the melt at 0 and 90 degrees C, respectively. The polymorphic transitions of the two samples induced by deformation at different temperatures (20, 40, and 60 degrees C) were investigated by rheo-optical FTIR spectroscopy. The results indicated that stretching leads to the transition from the helical to trans-planar conformation and improves the orientation of both helical and trans-planar conformations for the sPP films. With increasing stretching temperature, the conformational transitions for the two sPP samples are all suppressed, and the orientation behavior of the two samples appears completely different. The orientation degree of So decreases with increasing stretching temperature, while that of S-90 increases. These results suggest that the stretching temperature and initial structure have great influence on the conformation transition and orientation behavior of the sPP sample. On the basis of the experimental results, the schematic illustration of the conformation transition and orientation behavior of sPP during stretching has been proposed.