We recently showed nickel-underpotential deposition (Ni-UPD) occurs on polycrystalline or single crystal platinum electrodes in acidic media. Whereas the decoupling of the nickel and hydrogen adsorption/desorption peaks is difficult for low pH, these processes can be better separated for higher pH values, typically pH > 3. However, even for platinum single crystals, high pH solutions do not enable to sufficiently separate nickel from hydrogen phenomena. As a result, electrochemistry alone cannot yield important information about Ni-UPD, such as the formal partial charge number (valency of electrosorption) and the role of the sulphate or hydrogen sulphate anions. So, we decided to couple cyclic voltammetry to electrochemical quartz crystal microbalance (EQCM). EQCM measurements enable to decorrelate the simultaneous hydrogen and nickel adsorption/desorption peaks, which we could not attempt solely with electrochemistry. The coupling between gravimetric and electrochemical measurements allows us to detect the contribution of the anions and thus to isolate that of nickel: nickel coverage can then be determined. Nearly 4/5 Ni-UPD monolayer (theta(Ni) approximate to 0.8) over platinum is reached at nickel equilibrium potential for high pH solutions (5.5). The QCM and electrochemistry coupling further allows the determination of nickel formal partial charge number: t(Ni,EQCM) = 1.3 +/- 0.13. Direct electrochemistry measurements (Swathirajan and Bruckenstein method) yield: t(Ni,Pt(poly)) = 1.5 +/-0.17. These two values are close, which validates the electrochemical method for the nickel/platinum system. In consequence, we used Swathirajan and Bruckenstein method for Pt(1 10)-(1 x 2) crystal and found: t(Ni,Pt(1 1 0)) approximate to 1.4 +/- 0.1. Whatever the system (Ni-UPD/Pt(poly) or Ni-UPD/Pt(1 1 0)-(1 x 2)) or the experimental technique, nickel formal partial charge number is lower than nickel cation charge: t(Ni) < Z(Ni) = 2. In consequence, upon underpotential deposition on platinum surfaces, nickel cations discharge and then undergo additional charge exchange processes, such as anion (or water) adsorption, resulting in apparent partial nickel cation discharge. Moreover, Ni-UPD/Pt(1 10) surface displays high activity towards COad oxidation reaction. We explain such positive effect by the possible existence of a bifunctional mechanism in which oxygenated-species-covered NiUPD adatoms provide the oxygen atom to COad center dot center dot center dot Pt species, enabling its facile oxidation. (c) 2007 Elsevier Ltd. All rights reserved.