Journal of Applied Polymer Science, Vol.107, No.3, 1893-1899, 2008
Surface modification of CNFs via plasma polymerization of styrene monomer and its effect on the properties of PS/CNF nanocomposites
Carbon nanofibers (CNF) were modified via plasma assisted polymerization in a specially designed reactor. The effect of the plasma reactor conditions, such as power and time, on the extent of the CNFs modification was examined. Polystyrene (PS) coated nanofibers plus PS polymer were then processed in a Brabender torque rheometer mixing chamber to obtain PS/CNF nanocomposites, with 0.5, 1.0, 3.0, and 5.0 wt % of CNF. The effect of the plasma treatment on the dispersion of the nanofibers and on the compatibility between the nanofibers and the polymer matrix was also examined. Modification of the CNFs was assessed by measuring the contact angle of water in a "bed" of nanofibers and by examining its dispersion in several solvents. The morphology of PS/CNF nanocomposites was studied through scanning electron microscopy (SEM). Contact angles decreased in all cases, indicating a change in hydrophobicity of the modified CNFs. This change was confirmed in the CNF dispersion tests in several solvents. SEM micrographs show the difference between the original and the PS coated CNF. In addition, fractured samples show the effect of this treatment, in the sense that the CNF seem to be completely embedded in the polymer matrix, which clearly indicates the high compatibility between the PS and the modified (PS coated) CNF. As a consequence, a much better dispersion of the treated CNF was observed. Finally, the tensile modulus of PS/CNF composites increased slightly with respect to PS when using untreated CNFs, but more than doubled when using plasma treated CNFs. (c) 2007 Wiley Periodicals, Inc.