ZnO thin films are deposited on the glass substrates by sol-gel drain coating technique by varying the concentration of the sol. X-ray diffraction (XRD) and scanning electron microscopy (SEM) analysis were used to investigate the effect of sol concentration on the crystallinity and surface morphology of the films. The results show that with increase in sol concentration, the value of full width at half maximum (FWHM) of (0 0 2) peak decreases while the strain first increases and then decreases. The sol with higher concentration results in the increase in the grain size. The studies on the optical properties show that the band gap value increases from 3.27 to 3.3 eV when the sol concentration changes from 0.03 to 0.1 M. The photoconductivity studies reveal that the film for 0.05 M sol shows the maximum photoresponse for ultraviolet (UV) wavelength (<400 nm) which is co-related with the deep-level defects. The growth and decay of the photocurrent is found to be slowest for the same film. (c) 2007 Elsevier B.V. All rights reserved.