Density is an important parameter that influences the properties and performances of rigid polyurethane foam (PUF). Rigid PUF with different densities were prepared by varying the amount of distilled water as blowing agent. This investigation reports the mechanical, morphological, water absorption, thermal conductivity, and thermal behavior of rigid PUF varying with the density, which controls the foam architecture. The density of the PUF decreased from 116 to 42 kg/m(3) with an increase in the amount of water from 0.1 to 3.0 parts per hundred polyol by weight (phr), respectively. It was found that the mechanical properties of the PUFs changed with the foam density. The results of water absorption of the PUFs showed that water absorption increased with decrease in density, due to increase in the cell size and decrease in the cell-wall thickness. The thermal conductivity measurements showed that the thermal conductivity decreased with increase in density. It was due to the decrease in cell size. The thermal analysis of the PUFs shows that the glass transition temperature increases with the decrease in foam density, but the thermal stability decreases with the decrease in foam density. (c) 2008 Wiley Periodicals, Inc.