Biphasic calcium phosphate ceramics (BCP) has been widely used in tooth and bone implants due to its excellent biocompatibility. Incorporation of fluorine ions in BCP has drawn much attention because of the beneficial role played by the fluorine ions in bone and tooth growth. The aim of this study was to obtain fluoridated biphasic calcium phosphate (FBCP) by immersing BCP into saturated ZnF2 solution with F concentration of 3500 mg/l at different times. The phase and incorporation of fluoride into BCP were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and scanning electron microscope (SEM). The biomineralization and influence of FBCP on osteoblastic behavior were evaluated and compared with that of biphasic calcium phosphate (BCP). The results exhibited that the phase evolution of the BCP was affected by the fluoride incorporation and the FBCP significantly improved the differentiation and proliferation of osteoblasts. These findings suggest that the FBCP would be very useful as a bone reconstructive material. (c) 2008 Elsevier B. V. All rights reserved.